wear resistant coatings > flotation tank corrosion wearing compound ceramic coating

flotation tank corrosion wearing compound ceramic coating

BD7052 flotation cell anti chemical corrosion abrasion wearing resistant repair epoxy compound ceramic coatings

Product description:
BD7052 flotation tank repair epoxy compound anti wear abrasion corrosion chemical resistant coating is the high performance
abrasion wearing resistant polymeric material compounded by high performance wear resistant particle (silicon carbide,
carborundum etc.) and modified toughening wear resistant resin.Widely used in the repairing of the potion corrosion and
wear abrasion caused by mineral grains in the flotation cell,can also used in the preparation of wear/abrasion & corrosion
resistant pre-protective coating on the inner wall of flotation cell directly.

Product feature of our BD7052 anti chemical corrosion wear resistant flotation tank repair epoxy coating
1. With excellent wearing abrasion resistance,corrosion resistance
2. With very high bonding strength to various metal substrates
3. The facade doesn’t flow,construction is convenient,without high technical requirements for the constructors.
4. Suitable for the repairing and protecting of various wear abrasion,corrosion working condition.

Performance index of our BD7052 flotation tank epoxy repair compound abrasion corrosion
chemical resistant coatings

product name	Physics Status	operation time limit (25℃)	curing time (25℃)	range of application
BD7052 flotation cell reparing anti chemical corrosion wear resistant epoxy coating	paste	25 min	24 hours	Used in the repairing of corrosion, abrasion on the flotation cell which caused by potion and mineral grains,can also used in the preparation of wear & corrosion resistant pre-protective coating on the inner wall of flotation cell directly.

color	density (g/cm³)	compressive strength (kg/cm²) GB1041-2008	tensile strength (kg/cm²) GB6329-2008	shear strength (kg/cm²) GB7124-2008	bending strength (kg/cm²) GB1042-1999	hardness after curing （Shore D） ASTM-D-2556	working temperature （℃）
dark gray	1.75	930	335	130	490	89	-60-150

How to use
1.Surface treatment:
Do coarsening treatment on the pending-repair part,grinding with angle grinder or sand blasting etc,the surface after coarsening
treatment should be cleaned,the surface after this treatment should be the one coarsening,dry and fresh substrates,should be no
greasy dirt and dust.

2.Preparation of BD7052 flotation cell anti wearing corrosion chemical resistant repair coatings:
According to weight ratio A:B=4:1, make A and B two component mix uniformly,and use it up within 30 min.Generally it’s while
construction and configuration. According to the actual temperature,configuration can be properly a little more in winter,
proper less in summer.If the temperature is too low,can properly heat up the A component to reduce viscosity for easy to configure.

3.Coating:
The suitable coating thickness of BD7052 chemical abrasion corrosion resistant flotation tank repairing compound epoxy coating is
2~5mm.Make the mixed-up material be coating on the pending-repair part layer by layer,the first layer should be compacted,
make it infiltrate fully with the substrates.Repair the surface to be smooth after the coating is coated in the suitable size.

4.Curing:
It can be put into using after curing for 24 hours at the temperature of 25 degree.If the temperature is low,should heat it up or
prolong curing time to promote the curing.General construction in winter,can use iodine tungsten lamp do irradiation heating
with 40cm distance from the coating.

Packing specification:
1.Our common packaging:Two-component,20Kg/group,packed in a plastic drum.A component:16Kg/drum,B component:4Kg/drum.
2.We could offer you professional customized packaging and subpackage services based on users' requirements.

Transportation storage:
Sealed storage in the cool and dry place.The warranty period is 12 months.Avoid placing it upside down, knocking against and
transporting it as a non-dangerous product during transportation.

Special version:
1.This parameter is for laboratory conditions,due to the actual working condition is more complex,suggest the users to do the
pretest according to actual working condition.

2.When the environment temperature is below 15 degree,the curing time will prolong,should take proper heating measure.

3.When the environment temperature is more than 25 degree or the mixing quantity is too large,the curing speed will expedite,
should properly shorten the application time of coating after mixing.

Construction protective measures:
1.Wear the protective masks,wear the protective glasses and rubber gloves
2.Need washing hands with soap before eating,drinking or smoking.
3.The health hazard after touching: a few people will have skin allergy phenomenon,see a doctor in time and avoid touching with
this product again.should wipe it with ethyl acetate when the sizing material paste on the skin by careless,then wash it with clear water.
Should wash it with clear water immediately and see a doctor when splashing into the eyes by careless.

Warm Prompt:
Residual adhesive solution cured products are non-toxic harmless organic solid,but maybe it will produce poisonous gas
when burning,non-professional personnel can not do combustion disposal,should be sent to garbage power plant or garbage
burning place treatment.

Fire prevention measures:
Should choose dry powder to extinguish fire,can cover and flap it with dry powder,grit(the construction using abrasive)
or the non chemical fiber fabric when the sizing material catching fire.